Analisis Pengaruh Unsur Pemadu Terhadap Struktur Mikro Dan Kekerasan Pada Baja Laterit
Main Article Content
Abstract
Analysis of the influence of alloying elements on the composition of the appointment in the womb does not spread evenly on the steel samples of laterite, this is possible because the steel sample ketebalanpadadaerah laterite. At the micro structure of steel material hasilnyaadalahdaerah laterite classified as low, medium, high and this is caused because the carbon content in the area of ??steel material laterite percent lower alloying element content. Results microscopy analysis on steel samples of laterite by viewing the crystal grains with pembesaranmasing each 50 ?m and 30 ?m, showed the homogeneity of grains spread evenly. Basically the results of the domestic industry has been quite satisfactory in the quality control process pembuatannya.Namun seen in the test object lateritbentuk steel microstructure in the steel material lateritkurang evenly. In the test of the strength of the metal material has an advantage in the Brinell hardness test.
Downloads
Article Details
References
Adra.’’Pengujian Pengamatan Metalografi.’’Dalam http : //adra.biz/sain-Teknologi/Metalurgi/besi-baja iron-steel/pengujian pengamatan-metalografi/(17 Januari 2015)
Anshori,Yusuf 2013 .’’Pengertian Mesin Sekrap.’’Dalam http:// anshor 13041996.blogspot.com/2013/04/pengertian scrap.html(11 November 2014)
Buku Metalurgi Dan material 2010
Data Tahunan Pusat Penelitian Metalurgi dan Material
Diagram Fasa Fe3C Science and Technology dalam http://school007.ga//2013/04/ (11 Juni 2015)
Ikrom,zainul.2011’’.Mesin Gergaji’’.Dalam http://az-code.blogspot.com/2011/05/mesin-gergaji.html (24 November 2014)